Metal Ingot

Grade
Mg Ingot
Chemical composition
Mg
Fe
Si
Ni
Cu
Al
Ci
Mn
Others
MG99.98
99.98
0.002
0.003
0.002
0.0005
0.004
—
0.002
0.02
MG99.96
99.96
0.004
0.004
0.0002
0.002
0.006
0.003
0.003
0.04

Packing:
About 1000Kgs/Mg pallet covering with plastic bag, or according to customer’s requirement.
Ingot weight: 15Kg+/- 0.5kg; 7.5+/-0.5Kg ; 300g+/-50g

Category:

Related products

  • Quick View

    Aluminum Extrusion Scrap

    Item
    Standard(%)
    Result(%)
    Al
    balance
    99.99
    Si
    6.5-7.5
    6.73
    Cu
    0.1max
    0.0022
    Mn
    0.05max
    0.013
    Mg
    0.3-0.45
    0.381
    Ti
    0.2max
    0.14
    Zn
    0.05max
    0.013
    Read more
  • Quick View

    Pet Bottle Flakes

    PET bottle flakes – White clear color
    Process : Hot washed.
    Moisture : 0.5 % max.
    PVC content : 0.01-0.03 %.
    I.V. : 0.7 – 0.85.
    M.P. : 255 +/- 5 C.
    Color availability : Clear /Crystal
    Flakes size :10-12 mm.
    Foreign materials : 0.5 % max.
    BULK DENSITY: ~450kg/m3
    HS 3907 6000

    PET bottle flakes – Green color
    Process : Hot washed.
    Moisture : 0.5 % max.
    PVC content : 0.01-0.03 %.
    I.V. : 0.7 – 0.85.
    M.P. : 255 +/- 5 C.
    Color availability : Clear /Crystal
    Flakes size :10-12 mm.
    Foreign materials : 0.5 % max.
    HS 3907 6000

    Read more
  • Quick View

    OMG & OIMG Scrap

    Moisture :less 2%
    Free from rubber materials
    Free from other hard materials
    Packing:500kg per bale or according to buyer’s request
    ONP
    OINP
    Magazine
    OCC
    Sorted Office Paper
    Waste Yellow Pages Telephone directories
    Waste newsprint paper
    Mixed Paper

    Read more
  • Quick View

    Virgin/HDPE/LDPE/LLDPE/PP Resin/Granules/Pellets

    LDPE Injection Grade
    Tests
    		 
    Value
    		 
    Unit
    		 
    Melt Flow Rate   (MFR)
    		 
    15
    		 
    g/10min
    		 
    Density
    		 
    0.922
    		 
    g/cm3
    		 
    Tensile Yield   Strength
    		 
    7
    		 
    Mpa
    		 
    Elongation at Break
    		 
    75
    		 
    %
    		 
    Wien Softening   Point
    		 
    85
    		 
    °C
    		 
    Packing
    		 
    In 25 kg PP woven bags,20MT/20’FCL
    		 
    LDPE film grade
    Tests
    		 
    Value
    		 
    Unit
    		 
    Melt Flow Rate   (MFR)
    		 
    2
    		 
    g/10min
    		 
    Density
    		 
    0.9225
    		 
    g/cm3
    		 
    Tensile Strength
    		 
    9
    		 
    Mpa
    		 
    Elongation at Break
    		 
    500
    		 
    %
    		 
    Fish eye   max(0.3-2mm)
    		 
    30
    		 
    n/1200cm2
    		 
    Stripes
    		 
    20
    		 
    cm/20m3
    		 
    Packing
    		 
    In 25 kg PP woven bags,20MT/20’FCL
    		 
     Application:

 Packing film, net, cord; General purpose and industrial purpose, bottle, box; Agricultural irrigation pipe, hot water pipe; 

Greenhouse film goods bag; Burrier drainage pipe; PE pipe; For agricultural film, shrinkable film; all kinds of packaging bag; 
Injection molding, cast film; etc.

Film Grade HDPE
    Property
    		 
    Unit
    		 
    Typical Value
    		 
    Mass density
    		 
    g/cm 3
    		 
    0.941-0.959
    		 
    Melt flow Rate(190 centidegree /2.16kg)
    		 
    g/10min
    		 
    ≤1.0
    		 
    Tensile yield strength
    		 
    MPa
    		 
    ≥19.0
    		 
    Flexural modulus
    		 
    Mpa
    		 
    ≥965
    		 
    Elongation@ break
    		 
    %
    		 
    ≥400
    		 
    Impact Embrittlement temperature
    		 
    centidegree
    		 
    MAX -118
    		 
    Dielectric Constant
    		 
    100KHZ
    		 
    2.32
    		 
    
    		


    1MHZ
    
    		


    2.31
    
    		

    

    


    Loss Tangent
    
    		


    100KHZ
    
    		


    MAX 0.0001
    
    		

    

    


    
    		


    1MHZ
    
    		


    MAX 0.0001
    
    		

    

    


    Volume resistivity
    
    		


     OHM-CM
    
    		


    MIN 1x10 15
    
    		

    

    


    Application
    
    		


    Mainly used for the production of shopping bag, food bags, etc.
    
    		

    
    

    

    
        Read more
    •